• 专利标题:   Preparing multilayer stripping flower-shaped structure graphene oxide used as composite filler, by dispersing carbon material in sulfuric acid, adding potassium persulfate, heating, and stirring to obtain pre-oxidation product.
  • 专利号:   CN108059158-A
  • 发明人:   MO Z, ZHANG H, GUO R, FENG H, WANG R, YAN M
  • 专利权人:   UNIV NORTHWEST NORMAL
  • 国际专利分类:   C01B032/23
  • 专利详细信息:   CN108059158-A 22 May 2018 C01B-032/23 201838 Pages: 8 Chinese
  • 申请详细信息:   CN108059158-A CN11494560 31 Dec 2017
  • 优先权号:   CN11494560

▎ 摘  要

NOVELTY - The preparation method of multilayer stripping flower-shaped structure graphene oxide involves: (1) dispersing a carbon material in concentrated sulfuric acid, adding potassium persulfate, heating at 80-85 degrees C, carrying out stirring at a constant temperature for 4-5 hours to obtain a uniform pre-oxidation product, cooling to room temperature, dispersing the obtained product in ultrapure water, filtering, washing with ethanol and ultrapure water, and drying to obtain a pre-oxidized carbon material; and (2) adding pre-oxidized carbon material to a mixed solution of concentrated sulfuric acid and concentrated nitric acid, stirring at 0-5 degrees C for 10-15 minutes, uniformly mixing the reactants, slowly adding potassium chlorate to the mixture, carrying out stirring reaction at room temperature for 100-120 hours, dispersing the obtained product in ultrapure water, filtering, washing with ethanol and ultrapure water, and drying to obtain the product. USE - The method is useful for preparing multilayer stripping flower-shaped structure graphene oxide, which is useful as composite filler. ADVANTAGE - The method prepares multilayer stripping flower-shaped structure graphene oxide with good peeling effect and large specific surface area of 200-300 mu m. The prepared graphene oxide has wide application prospect in graphite oxide-related composite materials.