▎ 摘　　要

NOVELTY - Light emitting diode lamp radiating coating comprises 60-75 pts. wt. mixed resin, 3-4.5 pts. wt. sodium montmorillonite, 4-6.5 pts. wt. carboxylated styrene-butadiene latex, 1.5-2 pts. wt. silicone methyl branched silicone oil, 0.7-1.2 pts. wt. polyethylene glycol, 0.7-1.8 pts. wt. n-pentane, 1-2.5 pts. wt. nano-silica, 7-9 pts. wt. polyacrylonitrile-based carbon fiber, 5-6.5 pts. wt. graphene, 1-2 pts. wt. fumed silica, 5.5-7 pts. wt. flame retardant, 4-6 pts. wt. modified aromatic amine curing agent. USE - Light emitting diode lamp radiating coating. ADVANTAGE - The light emitting diode lamp radiating coating has good heat dissipation effect, certain effects of removing pollutants such as formaldehyde, toluene and total volatile organic compounds, achieves the traditional lamp radiating coating unction and has wide market prospects. DETAILED DESCRIPTION - Light emitting diode lamp radiating coating comprises 60-75 pts. wt. mixed resin, 3-4.5 pts. wt. sodium montmorillonite, 4-6.5 pts. wt. carboxylated styrene-butadiene latex, 1.5-2 pts. wt. silicone methyl branched silicone oil, 0.7-1.2 pts. wt. polyethylene glycol, 0.7-1.8 pts. wt. n-pentane, 1-2.5 pts. wt. nano-silica, 7-9 pts. wt. polyacrylonitrile-based carbon fiber, 5-6.5 pts. wt. graphene, 1-2 pts. wt. fumed silica, 5.5-7 pts. wt. flame retardant, 4-6 pts. wt. modified aromatic amine curing agent. Light emitting diode lamp radiating coating comprises 15-20 pts. wt. solvent, 0.1-0.15 pts. wt. cerium oxide, 1.5-2 pts. wt. active mineral powder and 1.5-2.5 pts. wt. traditional Chinese medicine essential oil. The mixed resin is a mixture of a phenolic resin and an epoxy resin, the mass ratio of the phenolic resin to the epoxy resin is 2: 1 to 3: 1. The length of the polyacrylonitrile-based carbon fiber is 0.01 mm. The flame retardant is a mixture of ammonium polyphosphate, melamine and expanded graphite, and mass ratio of the ammonium polyphosphate, melamine and expanded graphite is 2: 1.5: 1.3. The solvent is a mixture of diacetone alcohol and butyl ester, the mass ratio of diacetone alcohol and butyl ester is 3: 1-3: 2. The active mineral powder is a mixture of germanium stone, fluorite, tourmaline and zinc spinel in a weight ratio of 2.5: 3: 3.5: 1.7. The tourmaline is a mixture of magnesium tourmaline and lithium tourmaline in a weight ratio of 4: 3. The particle size of the active mineral powder is less than or equal to 15 mu m. The coating is prepared by weighingmixed resin, sodium montmorillonite, carboxylated styrene butadiene latex, silicone methyl branched silicone oil, polyethylene glycol, n-pentane, nano-silica, polyacrylonitrile-based carbon fiber, graphene, fumed silica. The flame retardant and the solvent are placed in a mixer, concentrated and stirred at 80 degrees C for a total of 40 minutes, and the mixture is stirred for 40 minutes until the mixture is taken out of the mixer to obtain a mixture A. 65-85 pts. wt. folia perillae acutae, 15-20 pts. wt. lavender, 15-20 pts. wt. Origanum oil, 4-6 pts. wt. purslane, 3-5 pts. wt. unbracteolated spurge root, 3-4 pts. wt. Salvia miltiorrhiza, 3-4 pts. wt. flaccid knotweed herb, 3-4 pts. wt. radix stemonae, 5-8 pts. wt. impurities are placed in a vacuum kettle at -20 degrees C for 2-3 hours, then placed in a microwave dryer pretreatment, where the drying time is 30-40 minutes, the microwave power is 17kw. The material processed is put into an ultrafine grinder and crushed to 60 meshes to prepare a powdered medicament powder. The raw material powder is placed into the extraction vessel supercritical carbon dioxide extraction device, adjusting the extraction pressure of 28MPa, the extraction temperature of 45 degrees C. Carbon dioxide flow is 1100L / h, dynamic extraction is performed for 2 hours. The crude oil is placed in a 5 degrees C environment for 70 minutes. The frozen crude oil is placed in a high-speed refrigerated centrifuge at a rotational speed of 17000r / min for 25 minutes, and the impurities are removed and placed in a vacuum oven at 85 degrees C for 3 hours to obtain a volatile oil B. 3-4 pts. wt. Ageratum, 4-6 pts. wt. negundo chastetree fruit, 15-20 pts. wt. fructus cnidii, 3-4 pts. wt. spina date seed, 15-25 pts. wt. Elm bark, 4-6 pts. wt. Houttuynia cordata, 3-5 pts. wt. Corydalis bungeana, 3-5 pts. wt. caulis polygoni multiflori, 1-3 pts. wt. peppermint, 1-3 pts. wt. musk, 1.5-2.5 pts. wt. sweet marjoram, 1.5-2 pts. wt. vanilla, 0.5-1 pts. wt. ambergris are washed and dried, put into an atomizer and crushed to 30 mesh. The deionized water is added for soaking for 5 hours, stirred, and dispersed and mixed thoroughly to prepare Chinese medicine mixture. The traditional Chinese medicine mixture is extracted at 80 degrees C for 2 hours. The distillate is collected, extracted with ether. The volume ratio of distillate and ether is 2.5: 1. The upper oil phase is taken, and then added with 0.13-0.2 pts. wt. anhydrous sodium sulfate for drying to obtain volatile oil C. The volatile oil B and volatile oil C are mixed well to prepare a mixed oil and stirred while adding wheat germ oil, essential oil, herb of geranium essential oil, lemon essential oil and grapefruit essential oil, stirred for 45 minutes, allowed to stand for 30 minutes, filtered to remove impurities to obtain essential oils of Chinese medicine. The mass ratio of the mixed oil to wheat germ oil, essential oil, herb of geranium essential oil, lemon essential oil and grapefruit essential oil is 2: 0.5: 0.5: 0.6: 0.4: 0.5. The traditional Chinese medicine essential oils and mixture A are mixed at 70-80 degrees C under stirring in a blender for 15 minutes to obtain a premix. The premix is added into a ball mill, and then adding cerium oxide, activated mineral flour and modified aromatic amine curing agent, and concentrated grinding for 4.5 hours, filtering to remove impurities to obtain the light emitting diode lamp radiating coating.