▎ 摘　　要

NOVELTY - A polypyrrole-manganese dioxide-coated graphite alkenyl gas gel electrode material comprises 10-20 pts. wt. graphene oxide, 10-20 pts. wt. glucose, 20-30 pts. wt. zinc chloride solution having concentration of 2-5 mol/l, 30-40 pts. wt. potassium permanganate, 80-100 pts. wt. ethanol, 3-5 pts. wt. silane coupling agent KH560, 20-30 pts. wt. pyrrole, 35-45 pts. wt. p-toluenesulfonic acid, 35-40 pts. wt. ammonium sulfate solution having concentration of 3-6 mol/l and 500-1000 pts. wt. distilled water. USE - Polypyrrole-manganese dioxide-coated graphite alkenyl gas gel electrode material. ADVANTAGE - The electrode material improves super capacitor than the capacitance, and has improved conductivity, impregnated with the electrolyte capacity and improved cycle performance. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for a method for preparing a polypyrrole-manganese dioxide-coated graphite alkenyl gas gel electrode material.