• 专利标题:   Aqueous-based coating comprises first component (comprised of polydopamine modified polyaniline/graphene composition) and second component (comprised of pigment, and defoamer).
  • 专利号:   CN109054475-A
  • 发明人:   LI W, YANG N, WANG W, LIU A, WANG X
  • 专利权人:   INST OCEANOLOGY CHINESE ACAD SCI
  • 国际专利分类:   C09D004/02, C09D004/06, C09D005/08, C09D007/63, C09D007/65, C08G073/02
  • 专利详细信息:   CN109054475-A 21 Dec 2018 C09D-004/02 201911 Pages: 9 Chinese
  • 申请详细信息:   CN109054475-A CN10767976 13 Jul 2018
  • 优先权号:   CN10767976

▎ 摘  要

NOVELTY - Aqueous-based coating comprises component A and B at a mass ratio of 1:5-50, where the component A comprises 0.05-5.5 pts. wt. polydopamine modified polyaniline/graphene composition and 1-10 pts. wt. deionized water, and the component B comprises 20-35 pts. wt. water-soluble alkyd resin, 5-15 pts. wt. copolymer multifunctional compound, 15-25 pts. wt. resin B, 5-10 pts. wt. pigment, and 1-5 pts. wt. defoamer. USE - Used as aqueous-based coating. ADVANTAGE - The coating is environment-friendly, has high-efficiency and anticorrosion, is a harsh and complex environment; ensures the interaction of heavy and corrosive environments, namely salt spray, damps heat and high in ultraviolet light in coastal wet and dry, which has have a impact on the performance and structural integrity of the sea immersed materials; has simple preparation process, low cost and high repeatability, and improves the service life of the coated steel, has low VOC content, small odor, safe and convenient to use, , excellent corrosion resistance and chemical resistance of the coating, small shrinkage, good hydrophobicity and high hardness. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for synthesizing the aqueous-based coating, comprising uniformly mixing the coating from a component of A and B in a ratio of 1:5-50, taking the component A including 0.05-5.5 pts. wt. polydopamine-modified polyaniline/graphene complex by weight, 1-10 pts. wt. deionized water, and component B including 20-35 pts. wt. water-soluble alkyd resin, 5-15 pts. wt. copolymer polyfunctional compound, 15-25 pts. wt. resin B, 5-10 pts. wt. pigments, and 1-5 pts. wt. defoamer.