▎ 摘　　要

NOVELTY - Preparing graphene conversion porous carbon microsphere comprises adding graphite oxide into deionized water for 30-300 minutes for ultrasound peeling to obtain graphene oxide dispersion; adding initiator after mixing uniformly, where the initiator is acid or alkali, and the concentration of the initiator is 0.01-5 mol/L; and sealing the steel with PTFE reaction kettle inner bag at 100-250 degrees C water for 2-40 hours, naturally cooling to room temperature, using deionized water to wash 3-6 times, drying, and preparing the porous carbon. USE - Method for preparing graphene conversion porous carbon microsphere (claimed). ADVANTAGE - The method is simple, and has low cost, short production period and easy mass production and application.