NOVELTY - An anode producing method involves mixing 30-70 pts. wt. cuprous chloride powder and 20-30 pts. wt. graphene nano-powder into a stirrer for 6-8 hours, adding 20-40 pts. wt. conductive carbon black, 1-5 pts. wt. anhydrous ethanol and 10-30 pts. wt. PTFE dispersion solution into the stirrer and stirring for 30-60 minutes to obtain dough mixture. The dough mixture is taken out, placed in a rolling mill for repeated rolling to obtain sheet with target thickness. The sheet is dried in oven at 70-95 degrees C for 1-4 hours, cooled at room temperature, and cut to desired size to obtain the finished product. USE - Method for producing anode of magnesium-cuprous chloride battery (claimed). DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for a magnesium-cuprous chloride battery.