• 专利标题:   Preparing graphene/polymer composite material involves taking polymer added to organic solvent A, stirring obtained mixture magnetically to dissolve, and then adding graphite oxide powder and organic solvent A.
  • 专利号:   CN106117852-A
  • 发明人:   MO Z, TAN D, WANG X, YIN Y, ZHAO J
  • 专利权人:   UNIV QINGDAO SCI TECHNOLOGY, ZHAO J, WANG X
  • 国际专利分类:   C08L025/06, C01B031/04, C08K003/04, C08L029/04, C08L077/00
  • 专利详细信息:   CN106117852-A 16 Nov 2016 C08L-025/06 201718 Pages: 5 Chinese
  • 申请详细信息:   CN106117852-A CN10158022 21 Mar 2016
  • 优先权号:   CN10158022

▎ 摘  要

NOVELTY - Graphene/polymer composite material preparation involves taking 1-10g polymer added to 10-100ml organic solvent A. The obtained mixture stirred magnetically to dissolve. 1-500mg graphite oxide powder and 1-100ml organic solvent A are mixed. The obtained mixture is dispersed uniformly. The two solutions are mixed. The obtained mixture is stirred. The obtained anti-solvent precipitation composite material is filtered, washed, and then dried. 1-100mg composite material and 1-10ml reducing agent are added into the reaction kettle. USE - Method for preparing graphene/polymer composite material (claimed). DETAILED DESCRIPTION - Graphene/polymer composite material preparation involves taking 1-10g polymer added to 10-100ml organic solvent A. The obtained mixture stirred magnetically to dissolve. 1-500mg graphite oxide powder and 1-100ml organic solvent A are mixed. The obtained mixture is dispersed uniformly. The two solutions are mixed. The obtained mixture is stirred. The obtained anti-solvent precipitation composite material is filtered, washed, and then dried. 1-100mg composite material and 1-10ml reducing agent are added into the reaction kettle. The obtained mixture is introduced with inert gas at 150 degrees C for 2-50 minutes with 25 megapascal to 24 Harbor Freight. The reaction kettle is kept in ice-bath. The obtained mixture is filtered, washed, and then dried.