• 专利标题:   Graphene offshore wind power blade coating comprises e.g. hydroxy acrylate, polyaspartic ester, pigment filler, dispersant, antifoaming agent, mildew inhibitor, graphene slurry, isocyanate tripolymer, graphene and thickening agent.
  • 专利号:   CN108676397-A
  • 发明人:   LI Z, WANG H, ZHAO W, WANG X, JIANG Q, WANG M
  • 专利权人:   MARINE CHEM RES INST CO LTD
  • 国际专利分类:   C09D004/02, C09D004/06, C09D005/08, C09D005/14, C09D007/61
  • 专利详细信息:   CN108676397-A 19 Oct 2018 C09D-004/02 201883 Pages: 11 Chinese
  • 申请详细信息:   CN108676397-A CN10340991 17 Apr 2018
  • 优先权号:   CN10340991

▎ 摘  要

NOVELTY - Graphene offshore wind power blade coating comprises component A comprises 10-40 wt.% hydroxy acrylate, 5-30 wt.% polyaspartic ester, 5-30 wt.% pigment filler, 0.2-1 wt.% dispersant, 0.2-1 wt.% antifoaming agent, 0.5-2 wt.% mildew inhibitor, 1-5 wt.% anti-rust pigment, 5-10 wt.% graphene slurry, and component B comprises 30-60 wt.% isocyanate tripolymer, graphene slurry is 0.5-5 wt.% graphene, 1-5 wt.% thickening agent, 0.5-5 wt.% silane coupling agent, 20-50 wt.% xylene, 20-40 wt.% butyl acetate and 15-40 wt.% poly(methyl acrylate) (PMA). The weight ratio of the components A and B is 2:1-4:1. USE - Used as graphene offshore wind power blade coating. ADVANTAGE - The coating has wear resistance, aging and rain erosion, anti-icing, high and low temperature resistance, salt spray resistance, heat and humidity resistance, and mold resistance.