• 专利标题:   Preparing biomass-based aerogel photo-thermal material used in seawater desalination, comprises mixing oxidized graphene in alkaline solution, adding cellulose and humic acid, mixing, adding cross-linking agent, mixing to form composite hydrogel, solvent exchanging, pre-freezing and freezing.
  • 专利号:   CN114350030-A, CN114350030-B
  • 发明人:   HUANG Y, QIU X, SUN L, ZHENG D
  • 专利权人:   UNIV SOUTH CHINA TECHNOLOGY
  • 国际专利分类:   B01J013/00, C02F001/14, C02F103/08, C08J003/075, C08J009/28, C08K003/04, C08L001/28, C08L097/00
  • 专利详细信息:   CN114350030-A 15 Apr 2022 C08L-001/28 202269 Chinese
  • 申请详细信息:   CN114350030-A CN11659012 30 Dec 2021
  • 优先权号:   CN11659012

▎ 摘  要

NOVELTY - Preparing biomass-based aerogel photo-thermal material comprises (i) adding oxidized graphene into alkaline solution, mixing uniformly, adding cellulose and humic acid, uniformly mixing to obtain mixed solution, then adding cross-linking agent and mixing uniformly, allowing to stand to form chemical cross-linked humic acid/cellulose/graphene oxide composite hydrogel; and (ii) subjecting the composite hydrogel to solvent exchange, pre-freezing and then freezing to dry aerogel. USE - The photothermal material is useful in seawater desalination (claimed). ADVANTAGE - The aerogel photo-thermal material: has a highly porous structure; provides a channel for the transport of water and steam; and has evaporation rate as high as 2.5 kg.m-2.h-1 when the light intensity is 1 kW.m-2. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for biomass-based aerogel photo-thermal material prepared by above mentioned method.