• 专利标题:   Artificial rock comprises rosin modified ethylene-vinyl acetate emulsion, graphene oxide, volcanic debris lava, micaceous schist, tensile reinforcing agent, processing auxiliary agent, dura fiber and hydroxyethyl cellulose.
  • 专利号:   CN108976577-A
  • 发明人:   WANG X
  • 专利权人:   HEFEI QIANYAO BUILDING DECORATION ENG CO
  • 国际专利分类:   C08K013/02, C08K003/00, C08K003/04, C08K003/34, C08L001/28, C08L023/08, C08L023/12, C08L075/06, C08L075/08, C08L093/04
  • 专利详细信息:   CN108976577-A 11 Dec 2018 C08L-023/08 201908 Pages: 7 Chinese
  • 申请详细信息:   CN108976577-A CN10565446 04 Jun 2018
  • 优先权号:   CN10565446

▎ 摘  要

NOVELTY - Artificial rock comprises 34-36 pts. wt. rosin modified ethylene-vinyl acetate (EVA) emulsion, 12-16 pts. wt. graphene oxide, 14-18 pts. wt. volcanic debris lava, 8-12 pts. wt. micaceous schist, 6-10 pts. wt. tensile reinforcing agent, 4-8 pts. wt. processing auxiliary agent, 4-8 pts. wt. dura fiber and 2-5 pts. wt. hydroxyethyl cellulose. USE - Used as artificial rock. ADVANTAGE - The artificial rock has tensile strength. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for preparing artificial rock, comprising (i) taking all raw materials; (ii) adding rosin-modified EVA emulsion, graphene oxide, volcanic debris lava and micaceous schist into the high-speed mixer in sequence, stirring at 550-750 revolutions/minute for 25-35 minute to obtain mixture A, sending obtained mixture A, tensile reinforcing agent, processing auxiliary agent, the dura fiber and hydroxyethyl cellulose into kneader and carrying out kneading extrusion; and (iii) subjecting extruded material to extrusion calendering, where temperature of the feeding section, the compression section and the homogenization section of the extrusion process are respectively 175 degrees C, 185 degrees C and 205 degrees C, and calendering at 165 degrees C and cooling.