▎ 摘　　要

NOVELTY - Epoxy group-modified silicone resin comprises 100-110 pts. wt. phenyl hydrogen-containing silicone resin, 0.3-0.6 pt. wt. catalyst, 100-110 pts. wt. solvent, 5-7 pts. wt. modifier and 0.2-0.3 pt. wt. polymerization inhibitor. The modifier is prepared by mixing gamma-aminopropyl triethoxysilane and octenyl succinic anhydride to N,N-dimethylformamide, adding graphene oxide and deionized water, dispersing for 10 minutes, mixing for 5 hours, adjusting pH to 10, washing with absolute ethanol and distilled water, drying to constant weight to obtain intermediate A, mixing intermediate A and N,N-dimethylformamide, adding tetrabutylammonium bromide and epichlorohydrin, reacting for 8 hours at 70?oC, cooling, washing and drying. USE - Epoxy group-modified silicone resin. ADVANTAGE - The silicone resin solves problems of poor system compatibility caused by adding epoxy coupling agent and tackifier.