▎ 摘 要
NOVELTY - Preparation of graphene-doped latex involves performing dissolution of raw glue, filtering to remove gel, adding dispersed graphene, adding crosslinking agent and crosslinking accelerator, dissolving to obtain crosslinking solution, mixing rubber solution, graphene suspension, crosslinking solution and water at mass ratio of 1:0.1-1:0.005-0.1:3-20, stirring at 800-1600 revolutions/minute (rpm) to obtain microemulsion, heating at 7-130 degrees C for 90-300 minutes, adding solvent, incubating, stirring at 900-2000 rpm to obtain homogeneous emulsion, concentrating, adding stabilizer and concentrating. USE - Method for preparing graphene-doped latex (claimed). ADVANTAGE - The graphene-doped latex is convenient to store, and has high stability.