• 专利标题:   Preparation of graphene-titania-clay composite material used in, e.g. sewage treatment, involves preparing graphene oxide and titania solution and subjecting prepared solutions and clay to hydrothermal treatment in reactor.
  • 专利号:   CN106824081-A
  • 发明人:   JIANG L, LI Y, YANG B, ZHANG Q, MIN Z
  • 专利权人:   UNIV XIHUA
  • 国际专利分类:   B01D053/86, B01J020/20, B01J020/28, B01J020/30, B01J021/18, B01J035/10, B01J037/10, C02F001/28, C02F001/30
  • 专利详细信息:   CN106824081-A 13 Jun 2017 B01J-020/20 201756 Pages: 8 Chinese
  • 申请详细信息:   CN106824081-A CN10128711 06 Mar 2017
  • 优先权号:   CN10128711

▎ 摘  要

NOVELTY - Preparation of graphene-titania-clay composite material, involves preparing graphene oxide suspension, mixing concentrated hydrochloric acid, water and ammonium sulfate, stirring, dripping tetrabutyl titanate in mixed solution, stirring for 2-3 hours to obtain titanium dioxide suspension, carrying out hydrothermal reaction, injecting graphene oxide suspension, titanium dioxide suspension and attapulgite clay to hydrothermal reactor at 160-200 degrees C, reacting for 20-24 hours to obtain three-dimensional composite material. USE - Preparation of graphene-titania-clay composite material used in sewage treatment and harmful gas purification. ADVANTAGE - The method provides graphene-titania-clay composite material, which has high electrical conductivity, recyclability, specific surface area, adsorption capacity, photocatalytic effect and purification ability. The composite material can be prepared industrially on a large scale by simple method. The method is economical and easy to operate. DETAILED DESCRIPTION - Preparation of graphene-titania-clay composite material, involves (a) preparing graphene oxide suspension, (b) mixing concentrated hydrochloric acid, water and ammonium sulfate, stirring, dripping tetrabutyl titanate in mixed solution, stirring for 2-3 hours to obtain titanium dioxide suspension, (c) carrying out hydrothermal reaction, injecting graphene oxide suspension, titanium dioxide suspension and attapulgite clay to hydrothermal reactor at 160-200 degrees C, reacting for 20-24 hours to obtain three-dimensional composite material. The volume ratio of graphene oxide suspension, titanium dioxide suspension and clay are 3-5:20-25: 0.006-0.01.