• 专利标题:   Anion anti-mold tile comprises diatomaceous earth metal, feldspar, clay, graphene, quartz, sodium silicate, magnesium oxide, lithium oxide, potassium oxide, calcium oxide, glaze and anti-mold agent.
  • 专利号:   CN107903036-A
  • 发明人:   HE H
  • 专利权人:   FOSHAN GAOMING PRODUCTIVITY PROMOTION
  • 国际专利分类:   C04B033/16, C04B033/13, C03C008/00
  • 专利详细信息:   CN107903036-A 13 Apr 2018 C04B-033/16 201834 Pages: 7 Chinese
  • 申请详细信息:   CN107903036-A CN11129457 15 Nov 2017
  • 优先权号:   CN11129457

▎ 摘  要

NOVELTY - Anion anti-mold tile comprises diatomaceous earth metal, feldspar, clay, graphene, quartz, sodium silicate, magnesium oxide, lithium oxide, potassium oxide, calcium oxide, and 2-sodium oxide, glaze and anti-mold agent, the glaze includes quartz, feldspar, marble, microcrystalline material, and negative ion powder, the negative ion powder is prepared from diatomaceous earth metal, high alumina mud, washed mud, medical stone, shell, tourmaline, bentonite, bauxite and coral fossils. USE - Used as anion anti-mold tile. ADVANTAGE - The tile has good oxidation; anti-corrosion; abrasion resistance; has a gem-like luster and health care function. DETAILED DESCRIPTION - Anion anti-mold tile comprises 100-120 pts. wt. diatomaceous earth metal, 30-40 pts. wt. feldspar, 35-40 pts. wt. clay, 10-15 pts. wt. graphene, 20-25 pts. wt. quartz, 15-20 pts. wt. sodium silicate, 1-2 pts. wt. magnesium oxide, 1-1.5 pts. wt. lithium oxide, 1-1.5 pts. wt. potassium oxide, 1-1.5 pts. wt. calcium oxide, and 2-2.5 pts. wt. 2-sodium oxide, 30-50 pts. wt. glaze and 2-5 pts. wt. anti-mold agent, the glaze includes 15-20 pts. wt. quartz, 15-18 pts. wt. feldspar, 5-10 pts. wt. marble, 8-12 pts. wt. microcrystalline material, and 4-6 pts. wt. negative ion powder, the negative ion powder is prepared from 5-8 pts. wt. diatomaceous earth metal, 2-5 pts. wt. high alumina mud, 1-3 pts. wt. washed mud, 5-10 pts. wt. medical stone, 1-2 pts. wt. shell, 3-5 pts. wt. tourmaline, 3-8 pts. wt. bentonite, 2-4 pts. wt. bauxite and 2-6 pts. wt. coral fossils, the anti-mold agent includes 20-30 pts. wt. mildew preventive, 1-2 pts. wt. fullerene, 10-12 pts. wt. polypropylene material, 1-2 pts. wt. silica material, 2-5 pts. wt. erucic acid material and 0.2-0.3 pts. wt. dispersing agent. An INDEPENDENT CLAIM is also included for preparing anion anti-mold tile comprising (1) making ceramic tile bodies, homogenizing the diatomaceous earth metal, feldspar and clay, adding water to the ball for 2-3 hours and sieving under 20 mesh to obtain the primary slurry, (a) mixing the primary slurry with the graphene, quartz, and sodium silicate and continuing ball milling for 8-10 hours to obtain a secondary slurry, (b) washing magnesium oxide, lithium oxide, potassium oxide, calcium oxide, and sodium oxide first with water, drying until the moisture content is 0.5%, freezing in a cold storage at -10 degrees C for 6-8 hours, and finally mixing secondary slurry and ball milling for 3-5 hours to obtain mud, (c) sieving slurry under 40 mesh, removing iron and adding into a decaying pool for 20-24 hours, spray-drying to a moisture content of 5-5.5% to obtain a powder, (d) sifting material under 80 meshes and adding into the warehouse, aging for 10-12 hours, (2) preparing glaze by adding quartz, feldspar, marble, microcrystalline materials, and anion powders and mixing, milling for 2-4 hours, carrying out ultrasonic emulsification at 25-35 kHz for 15-20 minutes, and continuing to mill for 3 hours, sifting through 50 meshes and aging for 18-22 hours, (3) using powder processed in step (1), pressing and forming, spraying the glaze to obtain a finished product and (4) adding anti-mold agent, mixing and coating on the surface of the finished product.