• 专利标题:   Preparing modified graphene quantum dots involves mixing graphene oxide, hydrogen peroxide and N,N dimethylformamide, subjecting resulting dispersion to solvothermal reaction to obtain GQDs (graphene quantum dots), mixing GQDs, 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride.
  • 专利号:   CN115849351-A
  • 发明人:   WU L, CAI F, CHEN G, GUO Y, ZHAO Q
  • 专利权人:   XIAMEN XIANGFUXING TECHNOLOGY CO LTD, UNIV HUAQIAO
  • 国际专利分类:   B82Y030/00, B82Y040/00, C01B032/184, C01B032/194, C09D175/14, C09D007/62, C09K003/00, G02B005/22, G02B005/30
  • 专利详细信息:   CN115849351-A 28 Mar 2023 C01B-032/184 202332 Chinese
  • 申请详细信息:   CN115849351-A CN11708068 29 Dec 2022
  • 优先权号:   CN11708068

▎ 摘  要

NOVELTY - Preparing modified graphene quantum dots involves mixing graphene oxide, hydrogen peroxide and N,N dimethylformamide. The resulting dispersion is subjected to solvothermal reaction to obtain GQDs, mixed the GQDs, 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride, and N-carboxysuccinimide at a pH value of 7-7.5 for activation to obtain the GQDs reaction solution. The GQDs reaction solution is mixed with aminoazobenzene compounds for amidation reaction to obtain a product. USE - Method for preparing modified graphene quantum dots. ADVANTAGE - The method changes the high light transmittance of the visible light region of the optical film itself and absorbs harmful blue light. DETAILED DESCRIPTION - INDEPENDENT CLAIMS are included for the following: 1. a graphene quantum dot/photocurable resin composite material, which comprises modified graphene quantum dot, resin, photoinitiator and diluent; 2. a polarizer, which comprises an optical film and a graphene quantum dot/photocurable resin composite coating on the surface of the optical film, where coating material of the graphene quantum dot/photocurable resin composite material is formed by the graphene quantum dot/photocurable resin composite material; and 3. a method for preparing polarizer, which involves: a. mixing the modified graphene quantum dots, resin, diluent and photoinitiator to obtain a mixed material; b. coating the obtained mixed material on the surface of the optical film, and curing under ultraviolet light to obtain a product.