• 专利标题:   Broadleaf concrete includes aluminum dihydrogen phosphate, dodecylbenzenesulfonate, sodium metasilicate, alum, broadleaf wood, mineral powder, and additive including graphene oxide, aluminum silicate fiber, and trifluoroacetic acid.
  • 专利号:   CN104058653-A
  • 发明人:   HU X, ZHANG X, ZHANG S
  • 专利权人:   BENGBU EAST CHINA GYPSUM CO LTD
  • 国际专利分类:   C04B016/02, C04B028/00
  • 专利详细信息:   CN104058653-A 24 Sep 2014 C04B-028/00 201501 Pages: 4 Chinese
  • 申请详细信息:   CN104058653-A CN10236433 30 May 2014
  • 优先权号:   CN10236433

▎ 摘  要

NOVELTY - Broadleaf concrete comprises 5-7 pts. wt. aluminum dihydrogen phosphate, 1.3-1.5 pts. wt. dodecylbenzenesulfonate, 8-10 pts. wt. sodium metasilicate, 3-5 pts. wt. alum, 30-40 pts. wt. broadleaf wood, 30-40 pts. wt. calcium carbonate powder, 5-7 pts. wt. carboxymethyl cellulose, 250-280 pts. wt. yellow sand, 170-190 pts. wt. cement, 540-570 pts. wt. gravel, 40-70 pts. wt. mineral powder, 20-30 pts. wt. additive and proper amount of water. The additive includes graphene oxide, aluminum silicate fiber, trifluoroacetic acid, dimethylaminoethyl acrylate, and cocoyl diethanolamide. USE - Broadleaf concrete. ADVANTAGE - The use of hardwood pulp increases the toughness and anti-cracking property of concrete. The use of additive increases the anti-folding strength resistance of concrete, increases the fragrance, and improves the anti-rust property, waterproof anti-seepage property, water reduction property, workability, plasticity and pumping effect. The concrete preparation method is simple and is suitable for industrial production. DETAILED DESCRIPTION - Broadleaf concrete comprises 5-7 pts. wt. aluminum dihydrogen phosphate, 1.3-1.5 pts. wt. dodecylbenzenesulfonate, 8-10 pts. wt. sodium metasilicate, 3-5 pts. wt. alum, 30-40 pts. wt. broadleaf wood, 30-40 pts. wt. calcium carbonate powder, 5-7 pts. wt. carboxymethyl cellulose, 250-280 pts. wt. yellow sand, 170-190 pts. wt. cement, 540-570 pts. wt. gravel, 40-70 pts. wt. mineral powder, 20-30 pts. wt. additive and proper amount of water. The additive comprises 0.5-0.8 pts. wt. graphene oxide, 6-7 pts. wt. aluminum silicate fiber, 1-1.3 pts. wt. trifluoroacetic acid, 1-2 pts. wt. allyl enanthate, 1-2 pts. wt. dimethylaminoethyl acrylate, 0.2-0.3 pts. wt. cocoyl diethanolamide, 0.4-0.6 pts. wt. methyl guaiacol, 2-3 pts. wt. butyl methacrylate, 1-2 pts. wt. 1,6-hexanediol diacrylate, 1-2 pts. wt. trimethylolpropane triacrylate, 5-7 pts. wt. magnesium oxide, 2-3 pts. wt. magnesium borate crystal whisker, 0.4-5 pts. wt. safflower, 0.1.8-1.02 pts. wt. sodium carbonate, 0.1-0.2 pts. wt. ammonium sulfate, 0.1-0.2 pts. wt. potassium persulfate, and 16-20 pts. wt. water. The concrete is prepared by mixing sodium carbonate, magnesium borate crystal whisker, cocoyl diethanolamide, graphene oxide, aluminum silicate fiber, trifluoroacetic acid, allyl enanthate, and dimethylaminoethyl acrylate, grinding and dispersing for 10-15 minutes, then adding water, heating to 70-80 degrees C, adding potassium persulfate, stirring for 20-30 minutes, reacting, mixing, heating to 80-90 degrees C, adding other residual components, stirring and reacting for 30-40 minutes to obtain the finished product.