• 专利标题:   Preparing natural graphite fast-charging lithium battery cathode material comprises e.g. uniformly mixing graphite precursor material, coating agent and graphene powder, heat treating in high temperature furnace, cooling, adding material into classifier to remove large particles, and graphitizing.
  • 专利号:   CN114671430-A
  • 发明人:   GU P, ZHAO J, GAO Y, WU H, ZHAO Y, LI X, HAN J, CHEN G, CHEN R
  • 专利权人:   LUOBEI AOXING NEW MATERIALS CO LTD
  • 国际专利分类:   C01B032/205, C01B032/21, H01M004/04, H01M004/36, H01M004/583, H01M004/62
  • 专利详细信息:   CN114671430-A 28 Jun 2022 C01B-032/205 202271 Chinese
  • 申请详细信息:   CN114671430-A CN10071298 21 Jan 2022
  • 优先权号:   CN10071298

▎ 摘  要

NOVELTY - Preparing natural graphite fast-charging lithium battery cathode material comprises (1) uniformly mixing the graphite precursor material, the coating agent and the graphene powder, (2) heat treating in a high temperature furnace for 4-10 hours under the protection of inert gas, and then cooling to room temperature, (3) adding the material into the classifier to remove large particles, (4) graphitizing the material at 2800-3200℃, (5) scattering and sieving the graphitized material, (6) mixing the sieved material and the binder in a certain proportion, (7) sending the mixed material to the carbonization furnace for carbonization at 600-1200℃, and (8) after demagnetization and sieving, obtaining the natural graphite fast charging lithium battery cathode material. USE - The method is useful for preparing natural graphite fast-charging lithium battery cathode material. ADVANTAGE - The method: improves the transfer speed of electrons and fast charging performance. DETAILED DESCRIPTION - Preparing natural graphite fast-charging lithium battery cathode material comprises (1) uniformly mixing the graphite precursor material, the coating agent and the graphene powder, (2) heat treating in a high temperature furnace for 4-10 hours under the protection of inert gas, and then cooling to room temperature, (3) adding the material into the classifier to remove large particles, (4) graphitizing the material at 2800-3200℃, (5) scattering and sieving the graphitized material, (6) mixing the sieved material and the binder in a certain proportion, (7) sending the mixed material to the carbonization furnace for carbonization at 600-1200℃, and (8) after demagnetization and sieving, obtaining the natural graphite fast charging lithium battery cathode material. The natural graphite fast-charging lithium battery cathode material comprises multiple particle composite particle structures, the surface of the composite particle structure is inlaid with graphene particles to form a network structure, and the mass ratio of the graphite precursor material, the coating agent and the graphene powder is 100:3-30:0.0001-0.01.