• 专利标题:   Manufacture of oxidized graphene-reinforced carbon air-gel material for adsorption and catalysis, involves dissolving resorcinol in water, adding catalyst and graphene oxide, adding formaldehyde solution, drying, and carbonizing.
  • 专利号:   CN103274384-A, CN103274384-B
  • 发明人:   LIAO B, LIU J, DENG L, GUO Q, ZENG F
  • 专利权人:   CHINESE ACAD SCI GUANGZHOU CHEM RES INST, FOSHAN FUNCTIONAL POLYMERIC MATERIAL
  • 国际专利分类:   B01J020/291, B01J020/30, C01B031/02
  • 专利详细信息:   CN103274384-A 04 Sep 2013 C01B-031/02 201381 Pages: 9 Chinese
  • 申请详细信息:   CN103274384-A CN10145468 24 Apr 2013
  • 优先权号:   CN10145468

▎ 摘  要

NOVELTY - 4-20 Pts. wt. Resorcinol is dissolved in 80-95 pts. wt. water, 0.008-0.07 pts. wt. catalyst mixture and 10-40 pts. wt. 1 %mass aqueous solution of graphene oxide, are added, 6-29 pts. wt. formaldehyde solution is added, sealed, dried, and carbonized to obtain oxidized graphene-reinforced carbon air-gel material. USE - Manufacture of oxidized graphene-reinforced carbon air-gel material for adsorption and catalysis (claimed). ADVANTAGE - The oxidized graphene-reinforced carbon air-gel material is easily manufactured with reduced energy consumption.