• 专利标题:   Preparation of coral-like palladium selenide compound used in catalysis, involves dispersing graphene oxide in deionized water and stirring evenly, adding palladium source, weak reducing agent, strong reducing agent and alkali to solution.
  • 专利号:   CN112573491-A, CN112573491-B
  • 发明人:   XIONG J, GUO Y, DU X, HUANG J, LEI T, CHEN W, YAN C, WU C, WANG X
  • 专利权人:   UNIV CHINA ELECTRONIC SCI TECHNOLOGY
  • 国际专利分类:   B82Y040/00, C01B019/04, C25B011/077
  • 专利详细信息:   CN112573491-A 30 Mar 2021 C01B-019/04 202141 Pages: 8 Chinese
  • 申请详细信息:   CN112573491-A CN11508881 18 Dec 2020
  • 优先权号:   CN11508881

▎ 摘  要

NOVELTY - Preparation of coral-like palladium selenide compound involves (1) dispersing graphene oxide in deionized water and stirring evenly, (2) adding a palladium source, a weak reducing agent, a strong reducing agent and an alkali to the solution obtained in step (1) in sequence, and mixing and stirring, (3) dissolving selenous acid in deionized water and stirring evenly, (4) mixing the solutions obtained in step (2) and step (3), and stirring evenly, (5) transferring the mixed solution obtained in step (4) to the reactor for hydrothermal reaction, and (6) cooling to room temperature naturally, and then filtering the solution to obtain a black precipitate, washing and freeze-drying to obtain the palladium selenide compound. USE - Preparation of coral-like palladium selenide compound used in catalysis application (claimed). ADVANTAGE - The one-step synthesis of coral-like palladium selenide compound nanomaterials by hydrothermal method has simple synthesis process, low toxicity, mild reaction conditions, low cost, and the synthesized Pd4Se has high purity.