• 专利标题:   Composite high-strength low-shrinkage cement-based material for use in modern building engineering, is prepared by combining graphene oxide-silicon dioxide and calcium carbonate micro powder, and adding into cement base material.
  • 专利号:   CN115572130-A
  • 发明人:   LI D, DENG X, SONG M, HU D, SHAN Y, ZHANG Y
  • 专利权人:   UNIV ANHUI TECHNOLOGY
  • 国际专利分类:   C04B111/20, C04B028/04
  • 专利详细信息:   CN115572130-A 06 Jan 2023 C04B-028/04 202309 Chinese
  • 申请详细信息:   CN115572130-A CN11261771 14 Oct 2022
  • 优先权号:   CN11261771

▎ 摘  要

NOVELTY - The method involves using TEOS as inorganic silicon source to prepare nano silicon dioxide, using intercalation method to introduce the nano SiO2 into the GO layer structure to prepare GO-SiO2 composite material, mixing the GO-Situ-CaCO3 micro powder to obtain the GO -SiO 2 -CaCO 3 composite powder, and then adding the GO, SiO 2 and CaCO3 composite powder and water reducing agent, sandstone aggregate into the cement gel material to obtain a needed high strength low shrinkage cement based material. USE - The composite high-strength low-shrinkage cement-based material is useful in a building material and in modern building engineering. ADVANTAGE - The composite high-strength low-shrinkage cement-based material has excellent mechanical property and durability, and reduces the cement base material drying shrinkage.