▎ 摘　　要

NOVELTY - Preparation of graphene oxide-zeolite molded material, involves dripping ultrapure water in graphene oxide powder and zeolite powder until the powder is completely wet, stirring well and adding to a ball mill, ball milling at 200-400 rpm for 3-6 hours, drying in a constant-temperature drying oven at 40-60 degrees C, and grinding to 50 mesh to obtain a graphene oxide-zeolite mixed powder, mixing the obtained mixed powder, carboxymethyl cellulose powder, and ultrapure water in a mass ratio of 2-5:1:7-11, stirring, and cutting and drying the obtained mixture at 40-60 degrees C according to the required specifications. USE - Preparation of graphene oxide-zeolite molded material used as adsorbent in water (sewage) treatment (claimed). ADVANTAGE - The method effectively combines graphene oxide and zeolite using carboxymethyl cellulose as binder, without affecting the original adsorption performance. The obtained product has excellent recyclability.