• 专利标题:   Preparation of boron carbide-titanium alloy composite armor involves mixing boron carbide powder and graphite powder, adding graphene solution, mixing, milling, granulating, drying, pouring into mold, hot pressing, and sintering.
  • 专利号:   CN108007273-A
  • 发明人:   XIA L, CUI Y, ZHAO L, FU S, FANG N
  • 专利权人:   ZHEJIANG LITAI COMPOSITE MATERIALS CO
  • 国际专利分类:   B22D019/08, B28B001/00, B28B003/02, C04B035/563, C04B035/622, F41H005/04
  • 专利详细信息:   CN108007273-A 08 May 2018 F41H-005/04 201837 Pages: 8 Chinese
  • 申请详细信息:   CN108007273-A CN11030328 27 Oct 2017
  • 优先权号:   CN11030328

▎ 摘  要

NOVELTY - Preparation of boron carbide-titanium alloy composite armor involves mixing 3-5 mu m boron carbide powder and 3-4% 1-2 mu m graphite powder; adding the graphene solution, mixing, and milling to form slurry; granulating, and drying; pouring into a mold, hot pressing, and sintering; splicing ceramic sheet into ceramic plate, placing the ceramic plate into the mold, preheating, and putting in a casting trough; and heating smelting furnace to a certain temperature, completely melting titanium alloy, casting into the ceramic plate, and solidifying. USE - Method for preparing boron carbide-titanium alloy composite armor. DETAILED DESCRIPTION - Preparation of boron carbide-titanium alloy composite armor comprises preparing 1-2 wt.% graphene oxide solution, adding dispersant, and uniformly dispersing to obtain evenly dispersed graphene solution; mixing 3-5 mu m boron carbide powder and 3-4% 1-2 mu m graphite powder; adding the graphene solution, mixing, and milling to form slurry; granulating, and drying; pouring into a mold, hot pressing, and sintering; splicing ceramic sheet into ceramic plate, placing the ceramic plate into the mold, preheating, and putting in a casting trough; and heating smelting furnace to a certain temperature, completely melting titanium alloy, casting into the ceramic plate, and solidifying.