▎ 摘　　要

NOVELTY - A transparent green glass comprises 304 kg quartz sand, 100 kg limestone, 61 kg kyanite, 9 kg aluminum hydroxide, 7 kg sodium nitrate, 8 kg magnesium carbonate, 6 kg borax, 0.5 kg graphene, 3.5 kg sodium fluorosilicate, 0.15 kg chloroplatinic acid, 0.024 kg potassium titanate whisker and 0.025 kg silicon carbide whisker. USE - Transparent green glass. ADVANTAGE - The glass has improved structural strength, transparency, hardness and resistance to high temperature. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for the preparation of weighing raw materials, mixing, ultrasonic dispersing for 1 hour, ball-milling with agate ball at mass ratio of 6:1 and speed of 150 revolutions/minute for 2 hours to obtain powder, placing powder into furnace, sealing, heating to 1720-1760 degrees C, maintaining temperature for 12-14 hours to obtain glass melt, feeding into molding machine, cooling to 400 degrees C, hardening, feeding into annealing furnace using conveyor, cooling to room temperature, feeding into steel annealing box, heating to 650-700 degrees C, stopping heating, rapidly cooling to room temperature by introducing cold air, tempering, and removing glass from steel box to obtain finished product.