• 专利标题:   Glass-fiber-reinforced PA66 power hardware material contains PA66, glass fiber, melamine cyanurate, zinc borate, aluminum hypophosphite, bamboo charcoal, carbon fiber, silicone rubber, aqueous polyurethane, and graphene oxide.
  • 专利号:   CN106566240-A
  • 发明人:   YU W, MA S
  • 专利权人:   MAANSHAN HUANENG ELECTRIC POWER LINE ACC
  • 国际专利分类:   C08J005/06, C08J005/08, C08J007/04, C08K013/06, C08K003/24, C08K003/32, C08K005/3492, C08K005/42, C08K007/06, C08K007/14, C08K007/24, C08L051/06, C08L075/04, C08L077/06, C08L083/04, C08L091/06, C09D175/04, C09D007/12
  • 专利详细信息:   CN106566240-A 19 Apr 2017 C08L-077/06 201740 Pages: 5 Chinese
  • 申请详细信息:   CN106566240-A CN10960874 04 Nov 2016
  • 优先权号:   CN10960874

▎ 摘  要

NOVELTY - A glass-fiber-reinforced PA66 power hardware material comprises PA66, glass fiber, melamine cyanurate, zinc borate, aluminum hypophosphite, bamboo charcoal, carbon fiber, silicone rubber, aqueous polyurethane, maleic-anhydride-grafted polypropylene, bovine serum albumin solution, potassium hexatitanate crystal whisker, graphene oxide, multiwalled carbon nanotubes, sodium dodecylbenzene sulfonate, paraffin wax, sodium tungstate, hydroxyacrylic resin, silica, aliphatic polyisocyanate, sodium hydroxide solution, ammonium bicarbonate, acetone, hydrochloric acid solution, and xylene. USE - Glass-fiber-reinforced PA66 power hardware material (claimed). ADVANTAGE - The hardware material has excellent antistatic property, corrosion resistance, and mechanical property. DETAILED DESCRIPTION - A glass-fiber-reinforced PA66 power hardware material comprises 32-40 pts. wt. PA66, 15-23 pts. wt. glass fiber, 3-7 pts. wt. melamine cyanurate, 2-5 pts. wt. zinc borate, 2-4 pts. wt. aluminum hypophosphite, 1-3 pts. wt. bamboo charcoal, 4-7 pts. wt. carbon fiber, 2-5 pts. wt. silicone rubber, 1-4 pts. wt. aqueous polyurethane, 2-4 pts. wt. maleic-anhydride-grafted polypropylene, 1-3 pts. wt. bovine serum albumin solution, 1-3 pts. wt. potassium hexatitanate crystal whisker, 1-2 pts. wt. graphene oxide, 2-5 pts. wt. multiwalled carbon nanotubes, 5-8 pts. wt. sodium dodecylbenzene sulfonate, 1-2 pts. wt. paraffin wax, 2-5 pts. wt. sodium tungstate, 2-5 pts. wt. hydroxyacrylic resin, 1-2 pts. wt. silica, 1-2 pts. wt. aliphatic polyisocyanate, sodium hydroxide solution, ammonium bicarbonate, acetone, hydrochloric acid solution, and xylene. An INDEPENDENT CLAIM is included for preparation of hardware material.