• 专利标题:   Aqueous wood lacquer having high adhesive force, comprises film-forming resin emulsion, titanium dioxide/graphene composite material, film-forming agent, matting powder, thickener, auxiliary agent, and deionized water.
  • 专利号:   CN115895362-A
  • 发明人:   ZHANG X, SUN X, LIN Z, ZHU H
  • 专利权人:   CHINA PAINT XINFENG CO LTD
  • 国际专利分类:   C09D133/00, C09D175/14, C09D007/20, C09D007/61
  • 专利详细信息:   CN115895362-A 04 Apr 2023 C09D-133/00 202335 Chinese
  • 申请详细信息:   CN115895362-A CN11485166 24 Nov 2022
  • 优先权号:   CN11485166

▎ 摘  要

NOVELTY - Aqueous wood lacquer having high adhesive force, comprises 60-85 wt.% film-forming resin emulsion, 0.1-1 wt.% titanium dioxide/graphene composite material, 2-4 wt.% film-forming agent, 1-3 wt.% matting powder, 0.5-2 wt.% thickener, 1-3 wt.% auxiliary agent, and deionized water (balance amount); where the film-forming resin emulsion is mixture of acrylic emulsion and polyurethane modified acrylic emulsion. USE - Used as aqueous wood lacquer. ADVANTAGE - The method: utilizes acrylic emulsion that is compounded with polyurethane modified acrylic emulsion, which reduces the addition amount of the polyurethane modified acrylic emulsion and save costs while improving the performance of the aqueous wood lacquer; improves the mechanical properties, adhesion, hardness and impact resistance of the aqueous wood lacquer by adding the titanium dioxide/graphene composite material; and reduces the volatile organic compound content and improves the environmental protection effect of the aqueous wood lacquer. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for preparing aqueous wood lacquer, comprising (1) preparing titanium dioxide/graphene composite material, and (2) mixing and stirring film-forming resin emulsion, titanium dioxide/graphene composite material, film-forming agent, matting powder, thickener, auxiliary agent and deionized water.