Preparing composite graphene oxide film, by applying mixed dispersion of graphene oxide water/nano-scale metal powder/carbon nanotubes to substrate, soaking substrate in coagulation liquid, drying, coating dispersion, soaking and drying.

MIN Y, LIU Y, JIAN L

Device capable of continuously producing graphene heat-conducting thin film, has conveyor belts located in charring furnace and in graphitization furnace which are arranged in meandering line.

MIN Y, HUI Z, DENG Y, CUI D, CAI Z

Preparation of composite protective solution, involves placing aniline solution in ice - containing water bath to obtain polyaniline aqueous solution, and preparing graphene oxide dispersion using expandable natural graphite.

CASTRO J, HUI Z, MIN Y, YU Y

Preparing graphene non-woven fabric used for storage devices and medical care involves dissolving graphene oxide fiber in water, and agitating with glass rod.

MIN Y, DENG Y, LIU Y, CUI D, HUI Z

Preparing graphene hollow fiber comprises e.g. preparing oxidized graphene dispersion with large layers of graphite as raw material, preparing graphene oxide by modified hummers, and selecting high speed centrifugation centrifugal liquid.

MIN Y, HUI Z, CAI Z, DENG Y, CUI D

Preparation of graphene modified polyimide composite film used in flexible circuit board, involves coating graphene-modified polyimide composite layer on surface of polyimide film.

MIN Y, WENG L, LIU Y, QI F, HE T

Preparation of graphene oxide using expanded graphite, involves reacting concentrated sulfuric acid and concentrated nitric acid with graphite to obtain graphite intercalation compound, and microwave reacting to obtain expanded graphite.

MIN Y, CUI D, ZENG W, CAI Z, YANG W

Preparation of large-scale graphene oxide, involves forming graphite intercalation compound using concentrated sulfuric acid, concentrated nitric acid and graphite, obtaining expanded graphite, reacting with strong acid, and oxidizing.

MIN Y, HUI Z, LIU Y, SHEN J, FENG Y

Preparation of large layer of graphene oxide with potassium perchlorate involves reacting graphite with strong acid, heating in microwave for expansion, re-treating with strong acid, and subjecting to oxidation stripping.

MIN Y, HUI Z, LIU Y, DENG Y, CUI D

Preparing highly oriented graphene fiber comprises taking a large layer of expandable natural flake graphite as raw material, preparing intercalation oxidation and the graphene spinning solution.

CAI J, LIU Y, MIN Y, ZHANG D, ZHAO C