Preparing carbon-coated tin selenide used as cathode material of potassium ion battery composite glue-linked three-dimensional graphene comprises e.g. mixing selenium powder, reducing solvent, carrying out hydrothermal reaction, separating, drying, performing uniform phase reaction and calcining.

HUO X, WANG Y, JI Y, HUANG J, LI J, WANG F, LIU W, CAO L

Preparing carbon-coated antimony selenide/graphene composite material involves adding graphene oxide into distilled water, and then adding antimony potassium tartrate, polyvinylpyrrolidone and carbon source under stirring.

HUANG J, GUO L, LUO T, CAO L, LI J, XU Z, FENG Y, WANG H

Preparing a honeycomb multi-stage pore nitrogen-sulfur-doped three-dimensional carbon material comprises e.g. slowly adding homogeneous solution containing trimeric thiocyanate to aqueous solution of graphene oxide to dissolve melamine.

HUANG J, XI Q, LI J, CAO L, CHENG Y, DANG H, WANG R, XU R

Preparing three-dimensional porous nitrogen-sulfur doped anode carbon material comprises e.g. slowly adding homogeneous solution of trithiocyanuric acid to aqueous solution of graphene oxide, uniformly stirring, drying, and calcining.

HUANG J, XI Q, LI J, CAO L, WANG T, WU W, XU P, GUO P

Production of in-situ three-dimensional porous carbon skeleton/graphene composite material used for sodium ion battery by soaking thin-walled plant skin in sulfuric acid, mixing with e.g. sodium carbonate, calcining, washing and filtering.

CAO L, HUANG J, LI J, OUYANG H, QI H, LI Q, LI R, CHENG Y, WANG C