Preparing carbon-coated tin selenide used as cathode material of potassium ion battery composite glue-linked three-dimensional graphene comprises e.g. mixing selenium powder, reducing solvent, carrying out hydrothermal reaction, separating, drying, performing uniform phase reaction and calcining.

HUO X, WANG Y, JI Y, HUANG J, LI J, WANG F, LIU W, CAO L

Preparing multi-level structure tetraoxide antimony graphene composite material used as cathode material of sodium ion battery, involves adding antimony tartrate into uniformly dispersed graphene oxide aqueous solution.

HUANG J, LUO T, GUO L, CAO L, LI J, XU Z, FENG Y, CHEN J

Preparing carbon-coated antimony selenide/graphene composite material involves adding graphene oxide into distilled water, and then adding antimony potassium tartrate, polyvinylpyrrolidone and carbon source under stirring.

HUANG J, GUO L, LUO T, CAO L, LI J, XU Z, FENG Y, WANG H

Preparing nickel-doped tungsten disulfide/graphene oxide composite electrode material used as battery negative electrode material, involves dispersing sodium tungstate dihydrate, and nickel nitrate hexahydrate uniformly in ethanol solution.

HUANG J, LUO X, CAO L, LI J, WANG Y, WANG F

Preparing vanadium-doped tungsten disulfide/graphene oxide composite electrode material as a battery negative electrode material, comprises dispersing graphene oxide and sodium metavanadate in water uniformly to obtain solution A.

HUANG J, LUO X, CAO L, LI J, WANG Y, WANG F

Preparing tin element composite tungsten disulfide/reduced graphene oxide composite electrode material as a battery negative electrode material, involves dispersing reduced graphene oxide, tungsten hexachloride and thioacetamide uniformly.

HUANG J, LUO X, CAO L, LI J, WANG Y, WANG F, GUO P

Preparing a honeycomb multi-stage pore nitrogen-sulfur-doped three-dimensional carbon material comprises e.g. slowly adding homogeneous solution containing trimeric thiocyanate to aqueous solution of graphene oxide to dissolve melamine.

HUANG J, XI Q, LI J, CAO L, CHENG Y, DANG H, WANG R, XU R

Preparing three-dimensional porous nitrogen-sulfur doped anode carbon material comprises e.g. slowly adding homogeneous solution of trithiocyanuric acid to aqueous solution of graphene oxide, uniformly stirring, drying, and calcining.

HUANG J, XI Q, LI J, CAO L, WANG T, WU W, XU P, GUO P

Preparation of molybdenum disulfide-graphite aerogel electrode material includes adding molybdenum trioxide and graphene oxide in distilled water, mixing, performing hydrothermal reaction, cooling, washing, separating and freeze-drying.

LIU H, DONG W, PANG L, LIANG Y, CHENG Y, WANG Z, CHEN N, ZHAO X