Preparing large sheet diameter graphene by under protection of inert gas, using three-electrode system, increasing potential from lowest potential of ion intercalation to highest potential of ion intercalation, performing constant potential electrolysis, and peeling-off.

WANG J, ZHANG Y, LIU R, XU Y

Self-adaptive electrochemical stripping method for preparing graphene, involves electrolyzing and peeling pre-inserted layer electrode in electrolyte according to preset voltage and preset current density to obtain graphene.

WANG J, WANG C

Preparing foamed nickel-supported graphene composite layered heterogeneous structure catalyst useful in electrolytic water hydrogen production, comprises e.g. adding ammonium tetrathiomolybdate to graphene oxide suspension, reacting, separating and purifying.

ZHAO W, LU W, FENG K, CHEN C, LUO Y, YU F, WANG J

Method for continuously preparing graphene oxide by two-step electrochemical method, involves connecting plug layer groove and oxidation groove to negative electrode supply through lead, and soaking inserting layer groove and oxidation groove in intercalation electrolyte.

LIU Y, CHENG H, HUANG K, WANG J, WEI T

Method for preparing oxidized graphene by adjusting pressure controllable electrolysis, involve using graphite raw material limited and extruded by mesh container space, and stripping and cleaning material positive electrode oxidation reaction to obtain graphene oxide materials.

LIU Y, CHENG H, HUANG K, WEI T, WANG J

Method for preparing metal cobalt nanoparticle nitrogen-doped graphene and carbon nano-fiber composite material, involves immersing cleaned bacterial cellulose film in mixed solution of urea and cobalt salts respectively.

XIAO L, SUN J, WANG J, CUI D

Gas diffusion layer formed by carbon fiber and graphene combination, comprises carbon fiber monofilament and graphene composite formed porous ventilating conductive carbon material layer.

WANG J

Preparation of nickel selenide-graphene composite material includes dispersing nickel dichloride hexahydrate and sodium citrate in deionized water, mixing nickel dichloride hexahydrate and sodium citrate with selenium solution and heating.

MO Z, LIU G, SHUAI C, NIU X, YANG X, WANG J, PEI H, GUO R, LIU N

Highly thermally conductive graphene or titanium composite material preparation involves preparing oxide graphene colloid, adjusting pH value, and then adding certain amount of electrolyte into oxide graphene colloid.

WANG H, WANG J, ZHANG W, YANG X, ZHONG B, ZHOU W

Forming graphene used in e.g. bioanalytics involves providing graphite sample having atomic layers of carbon; introducing solvent and ions into spaces between the atomic layers; expanding space; and separating the layers using driving force.

LOH K P, WANG J, JUNZHONG B, LOH K, LUO J, ZUNZHONG W