Preparation of composite material involves dispersing e.g. natural graphite and sodium cholate in deionized water, aging, centrifuging, filtering, drying, dispersing obtained powdered graphene in ethanol, adding aluminum powder and magnesium powder, stirring, drying, and sintering.

YANG F, LI Z, GUO X

Preparing graphene quantum dot reinforced aluminum-based composite material by using commercially available graphene oxide, producing three-dimensional network-shaped graphene through hydrothermal reaction, etching, evaporating, neutralizing, drying and preparing light brown graphene quantum dots.

DONG W, YAN X

Preparing high-strength plasticity titanium-graphene composite material based on hierarchical compounding, by weighing graphene powder material and titanium alloy powder respectively, and charging into ball milling tank for ball milling under argon gas and alcohol as process control agent.

DONG L, ZHOU L, CUI W, ZHANG Y

Preparing a titanium-graphene composite material with strong plasticity matching involves dispersing graphene oxide in a mixed solvent of deionized water and alcohol, mixing deionized water and alcohol according to a volume ratio.

DONG L, ZHOU L, CUI W, ZHANG Y

Continuous formation of reinforced aluminum strip material involves providing aluminum matrix material in powdered form, and reinforcing material in powdered form.

RAJESH K M, KHARE R, KHARE S, KSHIRSAGAR A M, MOHAN S R, RAGUNATH S, VIGNESHWARAN V, SAKTHIVEL D, JOE M D S, ASHOK K R