Preparing amino and pyrenyl group-modified alginic acid derivative useful in e.g. formaldehyde absorption, comprises e.g. acidifying sodium alginate, adding N,N'-dicyclohexylcarbodiimide, 4-dimethylaminopyridine, deionized water and ethylenediamine, freeze-drying, and adding 1-pyrenebutyric acid.

XIA Y, WANG X, LIU H, GONG X, LIU J

Material for e.g. all-weather seawater desalination, comprises hydrogel layer and hydrophilic film layer which are sequentially attached from top to bottom, where hydrophobic film layer is fiber fabric formed with photo-thermal nanoparticles.

ZHANG X, FENG K, CHEN L, GONG J, REN J, NIU R

Preparing graphene oxide/chitosan composite cadmium ion imprinted hydrogel, comprises e.g. preparing graphene oxide grafted polyacrylic acid, preparing polycarbonate microspheres, suction filtrating, drying and calcining, soaking product and carrying out cross-linking reaction.

ZHAO J, HU J, XU J, MU J

Preparing highly elastic hydrophobic graphene/nanocellulose composite aerogel comprises preparing graphene/nanocellulose composite hydrogel, preparing graphene/nanocellulose composite aerogel, and preparing highly elastic hydrophobic graphene/nanocellulose composite aerogels.

LI R, SHI B, HOU D, SONG F, HU W, GUO J, LI C

Preparing composite chromium ion-imprinted hydrogel involves using polycarbonate microsphere to obtain silicon dioxide hollow microsphere, preparing respectively thiolated graphene and alkyne-functionalized polyacrylamide, and using thiolated graphene and alkynyl functionalized polyacrylamide.

ZHAO J, HU J, XU J, MU J

Preparing polyimide composite foam material having photocatalytic performance, comprises e.g. adding polyamic acid, graphene oxide, prepared yttrium-manganese co-doped graphitic carbon nitride and prepared cerium-cobalt co-doped copper(I) phosphide into water, adding triethylamine, dispersing.

HUO X, GUO X, ZHANG M, TAO G, LIU P

Sound insulation material used in water purifying machine, comprises butyronitrile, modified oxidized graphene, zinc oxide, stearic acid, acceleratorand sulfur.

LI Z, MA X, YU W, WANG D, REN F