Preparing modified kaolin loaded graphene-phase carbon nitride/titania composite photocatalytic material, e.g. preparing porous graphite phase carbon nitride, and performing hydrothermal reaction with tetrabutyl titanate and hydrochloric acid modified kaolin in presence of aqueous ammonia.

CHEN W, ZHANG S, WANG T

Preparing palygorskite-titanium dioxide-graphene quantum dot composite photocatalyst water cracking hydrogen production comprises e.g. mixing nitric acid and deionized water to form dilute nitric acid solution, mixing isopropanol, titanate.

NIU J, LAI D, CHEN R, WANG D, ZHANG S, OU X, FENG P, QIANG Y

Preparing kaolinite-titanium dioxide-graphene composite photocatalyst having nano supporting pores, comprises e.g. mixing nitric acid, deionized water, isopropanol, titanate and diluted nitric acid solution, adding kaolinite and heating.

NIU J, CHEN R, LAI D, WANG D, ZHANG S, OU X, FENG P, QIANG Y

Preparing montmorillonite-titanium dioxide-graphene composite photocatalyst with column supporting structure useful e.g. for removing pollutant, comprises e.g. mixing nitric acid and deionized water to obtain dilute nitric acid.

NIU J, XIE J, WANG D, ZHANG S, OU X, FENG P, QIANG Y

Graphene oxide/titanium dioxide nano needle composite material for degradation of methylene blue wastewater, is prepared using graphene oxide as carrier, and loading titanium dioxide nanocomposites on graphene oxide surface.

HU L, LAI C, ZENG G, CHEN G, WAN J, ZHANG S, GUO Z, HUANG Z, HE K, WU J, LIU W

Preparation of three-dimensional graphene-nano titanium dioxide composite photocatalyst, involves immersing foamed nickel in aqueous graphene oxide solution, and processing to obtain oxidized graphene-loaded foamed nickel material.

CHEN G, CHAN G, LENG J, WANG Y, ZHOU G, ZHANG S, ZHAO S, SHAN G

Titanium dioxide-carbon and titanium dioxide-reduced graphene oxide light support film used for visible photocatalyst degradation of methylene blue, includes potassium titanium oxalate, diethylene glycol, cellulose paper and graphene oxide.

HU L, ZHANG S