Biocarbon composition comprises low-fixed-carbon material, high-fixed-carbon material, moisture and one or more additives, where low-fixed-carbon material and high-fixed-carbon material are present in biocarbon composition as homogenous physical blend and one or more additives include binder.

DAUGAARD D, SLACK D, MENNELL J A

Low-dimensional carbon material reinforced carbon graphite material used in e.g. aerospace application, comprises aggregate containing asphalt coke and carbon black, low-dimensional carbon material, modified asphalt and/or high-temperature asphalt as binder, and dispersion modifier.

LIU D, XU Y, HE Y, CHEN Y, TU C

Graphite crucible for electrode blank processing comprises graphitized coke, asphalt, and coating layer comprising resin and pyridine, and inert coating net is graphene with resin through coating bonding graphene side of coating is coated with resin graphene.

ZHANG Y, HU H, WANG J

Preparing high-performance anti-wear material added with sulfonated graphene useful as inorganic non-metal graphite sealing material by mixing superfine coke powder, graphite powder and graphene solution, adding asphalt, performing isostatic pressing treatment, roasting and graphitizing blank.

WANG Y, LIU W, MA Q, YIN J, LIANG S, DONG Z

Preparing selenium-graphene composite isostatic pressing graphite material as soft material used in industry, comprises e.g. obtaining aggregate, powder, binder, impregnating agent, and reduced selenium powder, mixing aggregate and powder, and mixing of mixed powder and selenium powder.

ZHANG Y, ZHANG P, GAO Z, MIN J

Optical fiber annealing tube used as structure in optical fiber drawing process, comprises coke primary powder, high temperature asphalt, and graphene micro-sheet powder.

QIU F, WU F, LAN Y, HUANG Y, LI Z

Method for preparing isostatic pressing product of graphene, involves calcining pressed molded product once in vacuum calcining furnace, and releasing after calcinations, and performing graphitization treatment on calcined product.

ZHANG P, WU C, CHAI W, WANG Z