Preparing composite wave absorbing material involves taking N,N-dimethylformamide and ethylene glycol in beaker, and mixing, weighing graphite oxide, sonicating, stirring, and adding nickel nitrate hexahydrate and zinc nitrate hexahydrate.

SHU R, DENG L, WU Y, LI X

Flexible, low shrinkage, conductive formulation for coating substrate of articles and filling gaps in electronic packages comprises sinterable, conductive metal particles, graphene, diluent, and polymer resin.

HONG X, SANCHEZ J G, CAO X, ZHUO Q

Manufacture of graphene-nano nickel thermoelectric thin film involves washing copper substrate with acetone, deionized water and methanol, placing substrate in container including uniform graphene solution, and performing electrophoresis.

LIU Y

Manufacture of graphene-supported nano-nickel thermoelectric composite film involves mixing sulfonated graphite, triblock copolymer and ammonium acetate, adding nickel chloride, heating, forming membrane and performing electrophoresis.

LIU Y

Preparation of graphene-nano nickel thermoelectric thin film involves preparing wave-absorbing material from oxidized graphite, adding deionized water, and performing electrodeposition on copper substrate using obtained solution.

LIU Y

Preparation of graphene-loaded nano-nickel thermoelectric composite thin film involves preparing wave-absorbing material from oxidized graphite, adding to deionized water and electrodepositing obtained solution on copper substrate.

LIU Y

Preparation of graphene-loaded nano-nickel thermoelectric composite thin film involves preparing wave-absorbing material from oxidized graphite, adding to deionized water and electrodepositing obtained solution on copper substrate.

LIU Y

Preparation of graphene-loaded nano-nickel thermoelectric composite thin film involves preparing wave-absorbing material from oxidized graphite, adding to deionized water and electrodepositing obtained solution on copper substrate.

LIU Y

Graphene-supported nano-nickel thermoelectric thin-film is obtained by preparing wave-absorbing material using e.g. surface-treated graphite oxide, mixing with water and depositing resultant on processed copper substrate.

LIU Y

Graphene-nano nickel composite thermoelectric thin film is prepared by adding solution containing graphite oxide into container, immersing pre-treated copper plate as negative electrode and iron sheet as positive electrode and reacting.

LIU Y