Nickel oxide and nickel composite graphene coated cotton carbon fiber material preparation involves immersing non-woven cotton in graphite oxide solution for sonication and then freeze-drying to obtain graphene coated non-woven cotton fiber.

ZHANG X, WANG Y, WEN G

Preparation of graphene/carbon nanofiber composite material used for detecting levodopa, by dissolving polyacrylonitrile powder in dimethylformamide solution, heating and stirring, electrostatic spinning, heating, stabilizing and cooling.

YUE H, WANG W, YU Z, GAO X, GUAN E, WANG Z, ZHANG H, SONG S

Pleated graphene fiber used for pleated graphene fiber nonwoven fabric is prepared by dissolving graphene oxide in solvent to obtain dispersion, adding copper hydroxide gel, dispersing, continuously wet spinning and vacuum drying.

YANG X, WANG F

Preparing color graphene fiber, comprises e.g. mixing graphene oxide dispersion liquid and centrifuging, injecting obtained solution in rotating coagulation bath, allowing to stand, drying, immersing in polyurethane solution and curing.

YIN Y, HUANG R, FAN L, WANG C, CHEN K

Porous graphene-based air purifying agent comprises organic titanate, soluble metal salt, silane coupling agent, graphene oxide, metal oxalate, melamine, foaming agent, polypropylene resin, inorganic acid, and solvent.

GUO C, WU X

Preparing tin oxide copper oxide composite graphene coated cotton carbon fiber material involves immersing natural cotton in graphene oxide solution, freeze-drying to obtain graphene oxide coated cotton fibers, dissolving stannous chloride.

ZHANG X, WANG Y, WEN G

Preparing porous graphene film involves preparing graphene dispersion, then adding polyamide and thickener under stirring, and carrying out vacuum distillation reaction and electrospinning reaction to obtain mixed graphene fiber.

JIANG L

Graphene composite fiber used as wire for e.g. light electric motors, has graphene inner core layer, and molecular protection layer that comprises halogenated hydrocarbon molecules combined with graphene in surface layer of graphene layer.

GAO C, LIU Y