Preparation of palladium-supported graphene-based catalyst includes dispersing graphite oxide in deionized water, replacing solvent in palladium-loaded graphene hydrogel with deionized water and freeze-drying.

ZHU C, ZHAO Y, ZHANG Y, ZHANG J, YANG B, HAI Y, QIU Z, LI P, XU J

Preparation of silver/graphene/zinc oxide composite material used for degrading of formaldehyde, involves adding zinc nitrate solution to sodium hydroxide solution, filtering precipitate, washing, drying and calcining dried precipitate.

MA L

Catalyst with ultra-small particles cobalt comprises ultra-small particle cobalt as active component and is uniformly dispersed on graphene carrier.

SHI P, QIN X, ZHANG F, WANG X, QIU H, YANG L

Preparation method of graphene catalytic network for catalytic oxidation of municipal wastewater, involves dispersing mixture of butyl titanate and sodium tungstate in ethanol solution, and dispersing, and dripping into ice water.

YANG P

Making core/graphene-based shell structure involves forming and optionally quenching composition of core nano- or microstructures and graphene-based structures having surface coated with curable organic material and curing organic material.

CHOPRA N, LOWREY J, ODEH I N

Preparation of catalyst used for photodegradation of organic pollutant, involves processing ceramic substrate with solution containing tetrabutyl titanate and graphene sol, loading with e.g. bismuth vanadate, drying and calcining.

LI C, LI Q, LI Z, YANG G

Preparing graphene immobilized enzyme catalyst for catalyzing grren synthesis of fatty acid ester, involves taking oxidized graphene aqueous solution, adding appropriate amount of sodium hydroxide, and sodium chloroacetate.

WEI L

Preparation of aerogel e.g. graphene aerogel of two-dimensional material, involves reducing temperature of suspension of two-dimensional material to below melting temperature of solvent having specified melting point and vapor pressure.

DERBY B, KINLOCH I, BISSETT M, CASANO CARNICER G, LIN Y, CASANO C G