Preparing graphene viscose composite fiber useful for composite fiber woven cloth, comprises e.g. pressing, stirring, heating, washing and drying, extruding and solidifying and electrospinning.

SONG H

Preparing graphene viscose composite fiber involves taking concentrated sulfuric acid, graphite, sodium nitrate in mass ratio, adding concentrated sulfuric acid to graphite and sodium nitrate in ice bath and stirring.

SONG H

Air purification nano fiber yarn window has nano fiber film that is covered on graphene coating layer, and nano fiber film that is covered on surface of glass fiber yarn window framework.

LIN S, ZHU H

Cobalt zinc sulfide/graphene/carbon nanofiber composite material used e.g. for electrode material is prepared by adding polyacrylonitrile powder in N,N-dimethylformamide solvent, stirring, electrostatic spinning and pre-oxidizing.

LIU T, ZHANG L, ZHANG Y, FAN W, MIAO Y, GU H

Porous carbon-doped graphene / iron oxide nanofiber lithium battery cathodematerial, comprises carbon, ferroferric oxide and graphite.

CUI S, DING B, HE J, WANG L, HAN Q, LIAN Y, TAN W

Preparation of poly(p-phenylene vinylene)/graphene composite nanofiber material involves reducing graphene oxide in graphene oxide and poly(p-phenylene vinylene) prepolymer mixed solution, into graphene, electrospinning, and sintering.

CHANG J, CHANG Q, LI Z, MA D, WANG C, WANG S, ZHANG N, ZHAO H, ZHAO X, SUN Z

Soft breathable thin film electrode material used for tactile sensor comprises polymer nanofiber and graphene, which are obtained by electrostatic spinning polymer solution and graphene oxide solution, and reducing graphene oxide.

LI B, XU C, ZHENG J

Preparation of polyvinylpyrrolidone/graphene composite nanofiber material involves mixing solution of graphene oxide and polyvinylpyrrolidone under high-energy ionizing radiation, reducing graphene oxide, and electrostatic spinning.

CAO X, CHANG J, CHANG Q, MA D, WANG C, WANG S, WANG P, ZHAO H, CAI Z, LI M