国家/地区 中国（8）
IPC部 C（8）
IPC大类 C08（8）
IPC小类 C08K（8） C08L（7） C08J（4）
IPC C08K003/04（7） C08J009/28（3） C08L079/08（3）
C08K003/22（2） C08K007/00（2） C08L023/12（2）
C08L063/00（2）
发明人 FAN W（3） FENG J（3） LIU T（3）
ZUO L（3） CHEN Z（2） DONG Y（2）
LU H（2） YIN E Y G（2） ZHANG Y（2）
公开年 2017（7）
申请年 2016（8）
专利权人 UNIV FUDAN（8）

Preparing polyimide-based composite gas gel comprises dispersing graphene oxide in deionized water, carrying out ultrasonic dispersion to obtain graphene oxide stable dispersion adding hydrazine hydrate and ammonia solution, and heating.

LIU T, ZUO L, ZHANG Y, FAN W, YIN E Y G, DONG Y

Graphene-reinforced polyimide-based composite aerogel comprises graphene and polyimide.

LIU T, ZUO L, ZHANG Y, FAN W, YIN E Y G, DONG Y

Preparing polyimide-graphene composite gel involves dissolving diamine in polar solvent and dispersing to ultrasonic state to obtain diamine solution, which is dispersed graphene oxide and stable dibasic amine-oxidized graphene.

LIU T, ZUO L, FAN W, GAO W, LU H, GU H, LAI F

Preparing graphene oxide composite proton exchange membrane by mixing aqueous dispersion of graphene oxide with polymer solution, ultrasonically processing and carrying out suction filtration and film formation reaction on dispersion.

JIA W, TANG B, WU P

Preparing composite material involves using polymer and graphene oxide as raw material, adding chemical reducing agent by conventional polymer processing method for reducing graphene oxide to obtain composite material.

FENG J, LIU Y

Preparing magnesium oxide-graphene composite heat-conducting insulating filler involves adding an aqueous magnesium salt solution to the aqueous solution of graphene oxide and adjusting pH value.

FENG J, CHEN Z, LU Q

Preparing magnesium oxide-graphene composite heat-conducting insulating filler involves adding an aqueous magnesium salt solution to the aqueous solution of graphene oxide and adjusting pH value.

FENG J, CHEN Z

Preparation of graphene-modified polymethyl methacrylate composite material with super high conductivity by mixing slightly oxidized expanded graphite mixed solution and hydrolyzed silane coupling agent solution and continuously reacting.

LU H, WANG P