Polyurethane elastomer composite material used in industrial field of serious abrasion problem, and in mining, petroleum and natural gas industry, comprises polyol, diisocyanate, chain extender, cross-linking agent, antimony compound, graphite derivative and fibre.

DING W, ZHAN S, LI W, SUN Z, XU T, WANG S

Preparing graphene-based hybrid flame retardant useful in fields of intelligent packaging and coating, comprises e.g. adding graphene oxide and de-ionized water to three-necked flask, and adding commercial flame retardant solution.

JIN Y, YANG H, DU W, WANG S

Wet-graphene polyurethane resin for synthetic leather, comprises polyester polyol, polyether polyol, chain extender, isocyanate, solvent, graphene, terminator, and additives and prepared by making polyester polyol and polyether polyol.

WANG S

Preparation of graphene-modified spandex fiber for use in, e.g. sportswear, involves mixing graphene material, chain extender, diisocyanate and diol with solvent, polymerizing to obtain polymer, mixing with dispersant, aging and spinning.

TANG D, YUAN Y, LV D, WANG S, XU R, SONG X

Polyurethane nano flame resistant composite material comprises polyether polyol reaction type flame retardant, graphene oxide grafted polyaniline, and catalyst and second component.

HAN Y, WANG S, LI T, WANG T, GAO X, ZHANG Z

Preparation of polyurethane modified graphene conductive coating used for coating leather, textile, wood or metal surface, includes mixing graphene oxide in deionized water, performing ultrasonic treatment and adding reducing agent.

DUAN B, DIAO S, DING H, WANG X, ZHANG M, WANG Q, WANG S, LUAN Z