Preparing bismuth oxyiodide/reduced graphene oxide binary composite material, involves using bismuth nitrate pentahydrate and potassium iodide as precursors, using water as solvent, adding reduced graphene oxide ethanol ultrasonic dispersion, and then undergoes hydrothermal preparation.

WU Y, ZHANG Y, LI Z, ZHANG M, WANG J, SUN J, YAO R, LI J, LV J, DU Y, CAO H, BAO Z

Catalyst used for preparing beta-carotene from vitamin A triphenylphosphine salt by electrochemistry, is a graphene-supported metal ferrite and a metal oxide catalyst.

ZHANG T, SONG J, SHEN H, JIE J, WANG J, ZHANG Y

Nickel zinc copper nanocomposite dehydrogenation catalyst comprises used for catalytic dehydrogenation of pyridine to synthesize 2,2'-bipyridyl redox graphene and nanocomposite of nickel zinc copper nitrogen-carbon core-shell nanospheres.

ZHOU Y, WANG J, BAO J, ZHANG Y, BU X, ZHANG Z, LIU W, WANG Y

Bifunctional heterogeneous palladium-MIL101-sulfonated graphene oxide composite material for beta-alkoxyalcohol catalytic synthesis, is prepared by stirring e.g. sulfonated graphene oxide, terephthalic acid and chromium nitrate nonahydrate.

ZHANG Y, TANG H, LI X, ZHOU M, WU Q, LIU D

Preparing black phosphorus-activated graphene heterojunction loaded nickel nitride particles by carrying out mechanical ball milling on black phosphorus nanosheet layer material and activating graphene nanosheet layer material.

XU Q, WANG X, ZHANG Y, YE W, FAN J, MIN Y

Preparing graphene-molybdenum disulfide/titanium dioxide complex material having an accordion structure useful as catalyst comprises e.g. preparing graphite oxide, washing, dissolving, vacuum drying, dispersing and transferring.

YANG C, LI J, ZHANG Y, WEN Z, ZHAO M, JIANG Q

Preparation of palladium-supported graphene-based catalyst includes dispersing graphite oxide in deionized water, replacing solvent in palladium-loaded graphene hydrogel with deionized water and freeze-drying.

ZHU C, ZHAO Y, ZHANG Y, ZHANG J, YANG B, HAI Y, QIU Z, LI P, XU J