Preparing graphene slurry comprises e.g. subjecting expandable graphite to high temperature expansion, pulverizing, mixing graphite powder with solvent, treating by high-speed shearing machine and performing ultrasonic treatment.

LI W, YUE X, LUO L

Graphite/graphene composite material for forming e.g. heat-collecting component, comprises flat-shaped graphite particles which are laminated such that basal surfaces are laminated over one another using graphene aggregates as binder.

MURAMATSU K, HOSOKAWA M

Preparing double-layer carbon based heat-conducting thin film, comprises e.g. subjecting graphene oxide solution to hydrothermal reduction reaction, and ball milling to obtain graphene based slurry, and coating on graphite paper.

WANG B, ZHANG Y

Preparation of ultrafine crystalline graphite powder, involves dispersing raw material including microcrystalline graphite powder in water to form slurry, adding quantum dots of graphene, ball milling, filtering slurry and drying.

LIN Q, LI L

Preparing ultrafine artificial graphite powder by adding graphene quantum dots to artificial graphite powder, carrying out wet ball milling, filtering to obtain slurry, and drying to obtain ultrafine artificial graphite powder.

QIANFENG L, LIPING L

Preparing ultra fine flake graphite powder involves preparing slurry by using flake graphite powder as raw material, adding graphene quantum dot which is crystalline flake graphite powder, carrying out for wet ball milling.

QIANFENG L, LIPING L

Graphene and nano-graphite sheet used for electronic, light and battery, prepared by dispersing graphite or synthetic graphite by specific liquid medium and anti-settling agent to have good fluidity.

DING C, FENG J