Preparing high-strength plasticity titanium-graphene composite material based on hierarchical compounding, by weighing graphene powder material and titanium alloy powder respectively, and charging into ball milling tank for ball milling under argon gas and alcohol as process control agent.

DONG L, ZHOU L, CUI W, ZHANG Y

Preparing titanium-graphene composite material comprises ball milling graphene powder material and titanium alloy powder in a ball mill set with tank filled with argon gas for protection, and performing densification sintering and molding.

DONG L, ZHOU L, CUI W, ZHANG Y

Preparing a titanium-graphene composite material with strong plasticity matching involves dispersing graphene oxide in a mixed solvent of deionized water and alcohol, mixing deionized water and alcohol according to a volume ratio.

DONG L, ZHOU L, CUI W, ZHANG Y

Preparing graphene-based cemented carbide composite self-lubricating coating comprises e.g. in-situ peeling to obtain graphene sheet, ball milling and plasma spraying graphene-based cemented carbide core-shell coating powder.

ZHANG Y, YU H, CHEN F, DONG F, ZHANG N, HE X, XU J, DU X, CHENG J

Preparation of lithium ion negative electrode material using tin-graphene composite material involves grinding tin, graphene, graphite and carbon black, performing graphitization, extruding, roasting, carbonizing, heating, and pressing.

WEI J, ZHANG J, MIN J, ZHANG P, PANG Z, WU J, LIU W, JI Y, XU B, LV X, LEI T, HUO Y, ZHANG Y, CHEN Y