Inserting two dimensional flakes of two dimensional material into pores of porous substrate, comprises providing porous substrate having open pores, applying liquid dispersion of flexible flakes to porous substrate and subjecting substrate.

KHRANOVSKYY E, ZHYBAK M

Gas diffusion layer formed by carbon fiber and graphene combination, comprises carbon fiber monofilament and graphene composite formed porous ventilating conductive carbon material layer.

WANG J

Graphene quantum dot used for preparing formulation, fiber product or in vivo implant for providing antibacterial effect, is prepared by mixing trinitrorylene with o-phenylenediamine, adding water and sodium hydroxide to obtain reaction system, uniformly mixing and performing hydrothermal reaction.

SHAN J, OU L, WU Z, XIA W, QI L

Preparation of environment-friendly special-shaped brush by mixing filler, rubber, propylene glycol, propylene glycol fatty acid ester, solid rubber, calcium silicate, linoleic acid and water and embedding brush wire into carrier.

HE F, CAO Y

Preparation of molybdenum oxide/carbon composite interlayer used for lithium ion battery, involves dissolving molybdenum source in mixed solvent, soaking carbon material in solution, high temperature processing, cooling and drying.

DING M, QU J

Preparing titanium dioxide/carbon composite interlayer, comprises preparing oxalic acid and sodium dodecyl benzene sulfonate water/ethanol solution, soaking carbon material into solution, and dissolving titanium source and acid in solution.

DING M, QU J

Industrial mass production of vertical graphene composite carbon felt involves soaking carbon felt in acid solution, vibrating, repeatedly washing soaked carbon felt with deionized water, drying, and putting carbon felt on roller device.

QIN C, LI T, WANG Q, LOU H, SHI L, LUO L, HUANG S

Preparation of fluorescent anti-counterfeiting coating comprises drying, pulverizing leather waste, dispersing in ultrapure water, hydrothermal reacting, suction filtering, compounding with thickener and printing code on substrate.

LI L, MA J, SHI J, ZHANG W

Preparing complex structured carbon material anti-oxidation coating by metal liquid phase, by adding active powder to substrate metal powder, mixing ethyl cellulose and water, grinding surface of carbon material, and adding carbon material to nitric acid aqueous solution for corrosion treatment.

SI X, GUO X, ZHAO S, LIU Y, WANG X, CAO J, LI C, FENG J

Preparation of graphene film, involves modifying functional group of graphite to obtain graphene oxide sheet, during which metal particles are reacted with carbon atom to form holes, and removing functional group by thermal reduction.

ZHOU B, TANG Z, ZHOU R, SU K