Preparing porous silicon nitride ceramic material, involves preparing graphene oxide aerogel from graphene oxide dispersion liquid and amino trimethylene phosphonic acid crosslinking agent using aqueous ammonia as alkali catalyst and adopting hydrothermal method.

TAN C, ZHANG C, LIN W

Preparing silicon nitride ceramic copper-clad plate for semiconductor component, involves weighing raw material alpha-silicon nitride, beta-silicon nitride, silicon carbide and sintering auxiliary agent, using silicon nitride graphene ball milling modification, and preparing mixed powder.

TAN C, LIU W, CHEN Z, ZHANG C, LIN W

Preparing graphene toughened and aluminum oxide composite ceramic, involves adding dispersion to high-temperature reaction vessel, carrying out solvent thermal reaction in reaction vessel to remove water and/or organic solvent in composite material and sintering.

CHEN X, LI J, LAI H, GE Z

Preparing core-shell type nano ceramic powder based on graphene coating used for modifying ceramic composite material, involves mixing polyamino cationic perylene bisimide graphene dispersant with deionized water, adding modified nano ceramic powder suspension into graphene dispersion, and stirring.

LI Y, XIE Y, FENG Z, XIN H, HU Y

Defective graphene/wave-transmitting ceramic composite wave absorbing material used as electromagnetic wave protection material, comprises defective graphene and wave-transmitting ceramics orderly deposited on surface of wave-transmitting nanowires.

ZHANG L, CAO Y, LIANG J, SONG Q, YE F