Preparing cast aluminum alloy water-soluble precision ceramic core, comprises sieving corundum powder, obtaining phenolic reaction system, forming viscous colloid, mixing and homogenizing corundum glue, graphene oxide mixture, phenolic resin, carbon powder and curing agent and warming.

LIANG C, HU J, ZHANG J, WU G, ZHAO L, LI Y

Preparing carbon/boron carbide composite material, used in industrial production, involves providing carbon compound, carbon fiber, boron compound, and binder perform pretreatment mixing procedure to form precursor, putting precursor into spray granulator and mixing precursor form injection material.

YEH S, CHEN Y

Environmentally-friendly cchromium-removing ceramic water reducing agent comprises polycarboxylate mother liquor, grinding aid, plasticizer, and reinforcing agent formed by mixing modified graphene and modified sodium alginate.

LUO W

Composite ceramic water reducing agent comprises polycarboxylate mother liquor, grinding aid, plasticizer, and reinforcing agent.

LUO W

Transparent nano air circulation ventilation structure integrated filter-removable functional mask, has mask body formed with multi nano-sized micro-holes, and filter removal groove formed on side of mask body.

JO S J, HWANG J S

Preparing selenium-graphene composite isostatic pressing graphite material as soft material used in industry, comprises e.g. obtaining aggregate, powder, binder, impregnating agent, and reduced selenium powder, mixing aggregate and powder, and mixing of mixed powder and selenium powder.

ZHANG Y, ZHANG P, GAO Z, MIN J

Special castable material useful for kiln mouth of cement kiln, comprises e.g. mullite, silicon carbide, calcium titanate aluminate, corundum, cement, aluminium oxide micro powder, silicon micro powder, silicon nitride powder, strontium titanate powder and sillimanite powder.

JIANG J, RUAN H, DONG S

Optical fiber annealing tube used as structure in optical fiber drawing process, comprises coke primary powder, high temperature asphalt, and graphene micro-sheet powder.

QIU F, WU F, LAN Y, HUANG Y, LI Z