Preparation of nitrogen-doped carbon nano-tube embedded with iron-cobalt oxide coated iron cobalt alloy heterogeneous particles for use as catalyst for zinc-air battery, involves heating nitrogen-doped carbon nano-tube embedded with iron-cobalt alloy particles to calcine, fully reacting, and cooling.

LI T, YAN Z, CAO W, MA Y

High-throughput laser synthesis method of graphene loaded nanoparticles useful as anode material of the lithium carbon dioxide battery by carrying out in-situ conversion polyimide polymer film or polyethyleneimine polymer film by laser, dropping metal precursor salt solution to substrate and drying.

WANG J, ZHANG J, XIE K, GUO C, HAN X

Preparation of carbon-coated ternary material used in lithium-ion battery, involves mixing nickel source, cobalt source, and manganese source into deionized water, adding lithium source and carbon source, and ultrasonically treating.

HAN Z, YAN X, CHEN X, GUO H, WANG Y, YANG Y, ZHANG W

Preparation of cobalt alkoxide used as lithium-ion battery negative electrode material, involves adding cobalt acetate and lithium hydroxide into ethylene glycol, heating, reacting at constant temperature, washing, filtering, and drying.

LIU J, HUANG S

Composite graphite material useful in lithium-ion battery, comprises porous graphite material, asphalt-based carbon material and nano-carbon material, where asphalt-based carbon material and nano-carbon material are filled in pores of porous graphite material.

LI H, LIU D, PANG W, DING L, GU H, PAN J, JIANG C

Preparing nano antimony/graphene composite material comprises mixing antimony oxide, graphene oxide and reducing agent through mechanical grinding to obtain antimony oxide/graphene oxide/reducing agent mixture, heating and washing the precursor product with water.

TAN L, YU G, ZHANG M, LIU Z, LIANG T, MA D, WANG W

Low-temperature and fast preparation of oligomeric graphene with large interlayer distance useful in cathode material for potassium ion battery, comprises preparing graphene oxide dispersion by Hummers method, drying, placing graphene oxide powder in tubular furnace and heating.

WANG Q, QIN M, YAN J

Preparing honeycomb-shaped multilayer graphene, comprises mixing potassium persulfate, phosphorus pentoxide and concentrated sulfuric acid, adding crystalline flake graphite, and mixing pre-oxidized graphite and sodium nitrate, and concentrated sulfonate and reacting to obtain precursor solution.

LIU J, ZHU Y, ZHAO R, PENG Y, QIU X, WU X

Sodium vanadium phosphate material with three-dimensional carbon framework useful in anode sheet of sodium ion battery.

JIANG Q, ZHANG J, WANG D, DONG Y

Positive electrode active material for calcium-ion battery, comprises sodium vanadyl fluorophosphate/reduced graphene oxide obtained by compounding sodium vanadyl fluorophosphate with reduced graphene and electrochemically removing sodium.

ZHOU L, MAI L, JIN S, AN Q