Transparent antistatic film useful in electronic devices, comprise substrate comprising first surface, and transparent graphene coating disposed on the first surface and comprising surface modified graphene nanosheets and carrier resin.

WU M Y, HSIEH C, SHEN F, CHEN T, JIAN Y, WU Y, XIE C, CHEN Z

Graphene sheet combining graphite flake structure used as heat-dissipation structure and in light and thin current electronic products, comprises graphite nanoplatelet material and graphene material mixed in the nanoplatelet material.

CHOU T, WU F, CHAN C, LIAO W, CHANG H, LI L, ROSS J, YU W F, CHIEH C C, HSIEN L W, PIN C H, JONG L L, WU F Y, CHAN C C, LIAO W H, CHANG H P, LI L J

Graphene dispersant used in e.g. preparation of graphene composite powder, and graphene composite film, comprises polyaniline oligomer or derivative which is electroactive polymer, and combines with graphene via pi-pi bond.

DAI L, GU L, YU H, ZHENG Y, MA J, ZHAO H, LIU S, DING J

Method for preparing battery electrode in e.g. printed electronics, involves spray-coating composite onto substrate to form battery electrode, where percentage of electroactive particles to graphene-based material is at specific amount.

CHU C, LI L, PUSHPENDRA K, HU L, KUMAR P, CHU C W, LI L J, HU L H, ZHU Z

Method of coating substrate e.g. metal product, involves mixing aqueous polymer dispersion comprising polymer and aqueous graphene dispersion, and coating mixture on surface of substrate and drying at predetermined temperature.

JIMENEZ GARCIA L, BIRNBRICH P, HENNIG I, CHA K C, SCHWAB M G, GERST M, JIMENEZ G L

Graphite-based carbon material used as graphene precursor for preparing graphene dispersion, comprises rhombohedral graphite layer and hexagonal graphite layer, and has specified rate calculated based on X-ray diffraction method.

HASEGAWA S, KAMIYA N, HASEGAWA SHOJI, KAMIYA NAGISA, SHOJI H, NAGISA K, SHEN Y

Graphite-type carbon raw material used as graphene precursor, has rhombohedral system graphite layer and hexagonal system graphite layer in ratio more than preset value, as measured using peak intensities specific planes of layers.

HASEGAWA S, KAMIYA N, SHOJI H, NAGISA K, HASEGAWA SHOJI, KAMIYA NAGISA, SHEN Y

Heat conducting composite material, useful in thermal garment, solar microwave water purifier, infrared paint or LED, comprises a matrix, and many graphene sheets respectively having two-dimensional planar structure.

LIN H, LIN I, LIN Y, SONG J, SUNG C, SUNG C M, LIN I C