Preparation of graphene involves preparing graphene oxide through Hummers oxidation method from flake graphite, adding alkali as catalyst and thiourea dioxide as reducing agent, carrying out reducing reaction, washing and drying.

BULIN C, ZHANG B, XING R

Preparation acetylacetone-polyvinyl alcohol-graphene nanocomposite material comprises mixing water, acetylacetone and polyvinyl alcohol, dissolving, adding polyethylene, graphite and crosslinking agent, and performing ultrasonic treatment.

WU P, TANG H, ZHANG B

Graphene-based composite material used as catalyst, is obtained by loading noble metal nanoparticles on surface of graphene oxide, and coating surface of graphene oxide loaded with noble metal nanoparticles by mesoporous silica.

WU L, TONG Z, SHANG L, ZHANG B, ZHANG D, ZHANG T

Preparing an iron coated multilayer graphene nanocomposite material, comprises peeling graphite oxide, and introducing pentacarbonyl iron into obtained multi-layer graphene and performing thermal decomposition process.

ZHANG B, HUANG Q

Preparing iron coated graphene nano composite material, comprises e.g. performing thermal expansion peeling treatment of graphite oxide to obtain multilayer graphene, placing into four-necked flask, stirring and mixing with organic solvent.