Lightweight, flexible graphite alkenyl composite absorbing film used e.g. in information, electronic and exploration field, is reduction-oxidation graphene oxide, iron(II,III) oxide nanoparticle compound and carbon fiber.

WANG X, YU X, YANG K, WANG T, MA C

Mixed solution useful for preparing elastic hydrophobic carbon nanotube-graphene composite aerogel, comprises graphene oxide, carboxy carbon nanotube, 0cross-linking agent, alkaline reducing agent and deionized water.

LIU H, MA Y, CHEN S, DING Z, HUANG Y

Preparation of carbon nanotube/graphene conductive hybrid material used for preparing conductive or antistatic polymer involves dispersing carbon nanotube in deionized water, mixing with graphene oxide, heating, and stirring.

WANG B, KONG Q, LUO Z, WANG Y

Bridging material useful for improving industrial graphene film layer comprises highly electric conductive bridging material having large length-to-diameter ratio of the one-dimensional nano material.

WANG Y

Preparing graphene/carbon nano tube composite material comprises manufacturing stage graphene oxide, providing graphene acid material into to the carbon nanotube fiber, and adding graphene acid bonding phase of the carbon nanotube fiber.

KIM Y, LIANG Z, YANG X

Working station system of carbon nano-tube composite material for producing graphene, comprises mixing tank configured graphene and carbon nano tube material, where material is conveyed to sand mill and grinding material set to middle tank.

LEI L, LIN S

Graphene composite airgel preparation involves dispersing graphene oxide in deionized water to form oxidized graphene dispersion, and then dispersing additive component in deionized water to form dispersion of added component.

XING G, HOU P, YANG Z

Preparing graphene/carbon nanotube reinforced and toughened carbon fiber composite material by dissolving destruction agent in strong acid, then adding graphite powder under evenly stirring, and dripping oxidizing agent under stirring.

WANG X

Graphene/carbon nanotube nano-laminated composite film used e.g. heat dissipation comprises graphene ultra-thin film formed on water surface and carbon nanotube ultrathin film pulled out of carbon nanotube array.

WANG J, XIE D

Preparation of nanoparticles/porous graphene composite used as electrode in batteries, involves dispersing graphene structures into solvent, adding nanoparticles precursors to dispersion and treating resultant precursor mixture.

XU J