Preparing conductive polymer/graphene oxide composite material involves dissolving ferric chloride in graphene oxide aqueous solution and dispersing ultrasonically to obtain mixed ferric chloride/graphene oxide aqueous solution.

YU X, WANG H, HE M, LI L, XIONG L

Preparing composite gel used for preparing capacitor, involves reacting graphene oxide and p-phenylenediamine are reacted to obtain graphene containing phenylamino group, and then subjecting The aniline and graphene.

LI L, HAN X, YU X, MU H, XIONG L, ZHANG Q

Preparation of polystyrene sulfonic acid grafted graphene/polyaniline conductive composite hydrogel used as molecular controlled release material includes adding graphene oxide, 2-bromoisobutyryl bromide and triethylamine and reacting.

LI L, LI Y, YU X, LIU Y, ZHANG Q

Silicon carbide/sulfonated graphene/polyaniline corrosion resistant coating comprises epoxy resin, silicon carbide/sulfonated graphene/polyaniline composite, curing agent, plasticizer, defoaming agent, and solvent.

LI L, LIU F, LIU Y, ZHANG Q

Preparation of sulfonated graphene/polyaniline composite material used as mercury ion absorbent in mercury ion containing wastewater, by subjecting water and natural graphite to chemical oxidization, and adding ammonium persulfate.

HU J, LI L, LV S, YAN H, ZHENG H, YU X

Graphene/conductive polymer composite film is obtained by dispersing oxidized graphite and conductive polymer in N-methylpyrrolidone, adding reducing agent, coating obtained solution on surface of substrate, washing and drying.

PAN J, LI L, YAO G, YU X, WEI Y